❞ كتاب Magnesium Technology 2013: Recrystallization Behavior of a MgAlCa Alloy during Thermomechanical Processing and Subsequent Heat Treatment ❝  ⏤ سوفين نايجل ماثودهو

❞ كتاب Magnesium Technology 2013: Recrystallization Behavior of a MgAlCa Alloy during Thermomechanical Processing and Subsequent Heat Treatment ❝ ⏤ سوفين نايجل ماثودهو

The Magnesium Technology Symposium, which takes place every year at the TMS Annual Meeting & Exhibition, is one of the largest yearly gatherings of magnesium specialists in the world. Papers are presented in all aspects of the field, ranging from primary production to applications to recycling. Moreover, papers explore everything from basic research findings to industrialization. Magnesium Technology 2011 covers a broad spectrum of current topics, including alloys and their properties; cast products and processing; wrought products and processing; forming, joining, and machining; corrosion and surface finishing; ecology; and structural applications. In addition, you'll find coverage of new and emerging applications in such areas as biomedicine and hydrogen storage.  
تعد ندوة تكنولوجيا المغنيسيوم ، التي تقام كل عام في الاجتماع والمعرض السنوي TMS ، واحدة من أكبر التجمعات السنوية لمتخصصي المغنيسيوم في العالم. يتم تقديم الأوراق في جميع جوانب المجال ، بدءًا من الإنتاج الأولي إلى التطبيقات إلى إعادة التدوير. علاوة على ذلك ، تستكشف الأوراق كل شيء من نتائج الأبحاث الأساسية إلى التصنيع. يغطي Magnesium Technology 2011 مجموعة واسعة من الموضوعات الحالية ، بما في ذلك السبائك وخصائصها ؛ منتجات الصب والمعالجة ؛ منتجات مشغولة ومعالجة؛ التشكيل والانضمام والتشغيل الآلي ؛ التآكل وتشطيب السطح ؛ علم البيئة. والتطبيقات الهيكلية. بالإضافة إلى ذلك ، ستجد تغطية للتطبيقات الجديدة والناشئة في مجالات مثل الطب الحيوي وتخزين الهيدروجين. 

Magnesium is a chemical element with the symbol Mg and atomic number 12. It is a shiny gray solid which bears a close physical resemblance to the other five elements in the second column (group 2, or alkaline earth metals) of the periodic table: all group 2 elements have the same electron configuration in the outer electron shell and a similar crystal structure.
المغنيسيوم هو عنصر كيميائي يحمل الرمز Mg والرقم الذري 12. وهو مادة صلبة رمادية لامعة تحمل تشابهًا ماديًا وثيقًا مع العناصر الخمسة الأخرى في العمود الثاني (المجموعة 2 ، أو معادن الأرض القلوية) من الجدول الدوري: الكل عناصر المجموعة 2 لها نفس التكوين الإلكتروني في غلاف الإلكترون الخارجي وبنية بلورية مماثلة.

Magnesium is the ninth most abundant element in the universe. It is produced in large, aging stars from the sequential addition of three helium nuclei to a carbon nucleus. When such stars explode as supernovas, much of the magnesium is expelled into the interstellar medium where it may recycle into new star systems. Magnesium is the eighth most abundant element in the Earth's crust and the fourth most common element in the Earth (after iron, oxygen and silicon), making up 13% of the planet's mass and a large fraction of the planet's mantle. It is the third most abundant element dissolved in seawater, after sodium and chlorine.
المغنيسيوم هو تاسع أكثر العناصر وفرة في الكون. يتم إنتاجه في النجوم الكبيرة والشيخوخة من الإضافة المتسلسلة لثلاث نوى هيليوم إلى نواة الكربون. عندما تنفجر مثل هذه النجوم على شكل مستعرات عظمى ، يتم طرد الكثير من المغنيسيوم إلى الوسط بين النجوم حيث يمكن إعادة تدويره إلى أنظمة نجمية جديدة. يعد المغنيسيوم ثامن أكثر العناصر وفرة في القشرة الأرضية  ورابع أكثر العناصر شيوعًا في الأرض (بعد الحديد والأكسجين والسيليكون) ، ويشكل 13٪ من كتلة الكوكب وجزءًا كبيرًا من غطاء الكوكب. وهو ثالث أكثر العناصر المذابة وفرة في مياه البحر ، بعد الصوديوم والكلور.

Abstract

Micro structure refinement via static and dynamic recrystallization
during thermomechanical processing is crucial to the development
of wrought magnesium product with desirable combinations of
strength and ductility. Micro structural evolution in thixomolded
AXJ810 is investigated during warm rolling and subsequent
annealing at 300°C and 450°C using scanning electron
microscopy and electron backscatter diffraction. The rolled sheets
exhibited a partially recrystallized micro structure with a strong
basal texture. Significant grain refinement was observed during
both static and dynamic recrystallization. Retarded grain growth
and strong texture randomization were observed only in regions
containing intermetallic particles.
سوفين نايجل ماثودهو - سوفين نايجل ماثودهو دكتور جامعى كرسي ، علوم وهندسة المواد مهندس ميكانيكى
من كتب التكنولوجيا والعلم - مكتبة كتب الهندسة و التكنولوجيا.

The Magnesium Technology Symposium, which takes place every year at the TMS Annual Meeting & Exhibition, is one of the largest yearly gatherings of magnesium specialists in the world.

نُبذة عن الكتاب:
Magnesium Technology 2013: Recrystallization Behavior of a MgAlCa Alloy during Thermomechanical Processing and Subsequent Heat Treatment

2013م - 1442هـ
The Magnesium Technology Symposium, which takes place every year at the TMS Annual Meeting & Exhibition, is one of the largest yearly gatherings of magnesium specialists in the world. Papers are presented in all aspects of the field, ranging from primary production to applications to recycling. Moreover, papers explore everything from basic research findings to industrialization. Magnesium Technology 2011 covers a broad spectrum of current topics, including alloys and their properties; cast products and processing; wrought products and processing; forming, joining, and machining; corrosion and surface finishing; ecology; and structural applications. In addition, you'll find coverage of new and emerging applications in such areas as biomedicine and hydrogen storage.  
تعد ندوة تكنولوجيا المغنيسيوم ، التي تقام كل عام في الاجتماع والمعرض السنوي TMS ، واحدة من أكبر التجمعات السنوية لمتخصصي المغنيسيوم في العالم. يتم تقديم الأوراق في جميع جوانب المجال ، بدءًا من الإنتاج الأولي إلى التطبيقات إلى إعادة التدوير. علاوة على ذلك ، تستكشف الأوراق كل شيء من نتائج الأبحاث الأساسية إلى التصنيع. يغطي Magnesium Technology 2011 مجموعة واسعة من الموضوعات الحالية ، بما في ذلك السبائك وخصائصها ؛ منتجات الصب والمعالجة ؛ منتجات مشغولة ومعالجة؛ التشكيل والانضمام والتشغيل الآلي ؛ التآكل وتشطيب السطح ؛ علم البيئة. والتطبيقات الهيكلية. بالإضافة إلى ذلك ، ستجد تغطية للتطبيقات الجديدة والناشئة في مجالات مثل الطب الحيوي وتخزين الهيدروجين. 

Magnesium is a chemical element with the symbol Mg and atomic number 12. It is a shiny gray solid which bears a close physical resemblance to the other five elements in the second column (group 2, or alkaline earth metals) of the periodic table: all group 2 elements have the same electron configuration in the outer electron shell and a similar crystal structure.
المغنيسيوم هو عنصر كيميائي يحمل الرمز Mg والرقم الذري 12. وهو مادة صلبة رمادية لامعة تحمل تشابهًا ماديًا وثيقًا مع العناصر الخمسة الأخرى في العمود الثاني (المجموعة 2 ، أو معادن الأرض القلوية) من الجدول الدوري: الكل عناصر المجموعة 2 لها نفس التكوين الإلكتروني في غلاف الإلكترون الخارجي وبنية بلورية مماثلة.

Magnesium is the ninth most abundant element in the universe. It is produced in large, aging stars from the sequential addition of three helium nuclei to a carbon nucleus. When such stars explode as supernovas, much of the magnesium is expelled into the interstellar medium where it may recycle into new star systems. Magnesium is the eighth most abundant element in the Earth's crust and the fourth most common element in the Earth (after iron, oxygen and silicon), making up 13% of the planet's mass and a large fraction of the planet's mantle. It is the third most abundant element dissolved in seawater, after sodium and chlorine.
المغنيسيوم هو تاسع أكثر العناصر وفرة في الكون. يتم إنتاجه في النجوم الكبيرة والشيخوخة من الإضافة المتسلسلة لثلاث نوى هيليوم إلى نواة الكربون. عندما تنفجر مثل هذه النجوم على شكل مستعرات عظمى ، يتم طرد الكثير من المغنيسيوم إلى الوسط بين النجوم حيث يمكن إعادة تدويره إلى أنظمة نجمية جديدة. يعد المغنيسيوم ثامن أكثر العناصر وفرة في القشرة الأرضية  ورابع أكثر العناصر شيوعًا في الأرض (بعد الحديد والأكسجين والسيليكون) ، ويشكل 13٪ من كتلة الكوكب وجزءًا كبيرًا من غطاء الكوكب. وهو ثالث أكثر العناصر المذابة وفرة في مياه البحر ، بعد الصوديوم والكلور.

Abstract

Micro structure refinement via static and dynamic recrystallization
during thermomechanical processing is crucial to the development
of wrought magnesium product with desirable combinations of
strength and ductility. Micro structural evolution in thixomolded
AXJ810 is investigated during warm rolling and subsequent
annealing at 300°C and 450°C using scanning electron
microscopy and electron backscatter diffraction. The rolled sheets
exhibited a partially recrystallized micro structure with a strong
basal texture. Significant grain refinement was observed during
both static and dynamic recrystallization. Retarded grain growth
and strong texture randomization were observed only in regions
containing intermetallic particles. .
المزيد..

تعليقات القرّاء:

تكنولوجيا المغنيسيوم والألمنيوم المؤتمر الوطني العراقي

سبائك المغنيسيوم والتكنولوجيا

تكنولوجيا المغنيسيوم وسبائكه وتطبيقاتها

المغنيسيوم وسبائكه تكنولوجيا وتطبيقات pdf

التكنولوجيا والمغنيسيوم

technology magnesium and aluminum    

magnesium alloys and technology    

magnesium - alloys and technology pdf    

magnesium technology metallurgy design data applications    

magnesium and its alloys technology and applications

magnesium and its alloys technology and applications pdf    

The Magnesium Technology Symposium, which takes place every year at the TMS Annual Meeting & Exhibition, is one of the largest yearly gatherings of magnesium specialists in the world. Papers are presented in all aspects of the field, ranging from primary production to applications to recycling. Moreover, papers explore everything from basic research findings to industrialization. Magnesium Technology 2011 covers a broad spectrum of current topics, including alloys and their properties; cast products and processing; wrought products and processing; forming, joining, and machining; corrosion and surface finishing; ecology; and structural applications. In addition, you'll find coverage of new and emerging applications in such areas as biomedicine and hydrogen storage.  
تعد ندوة تكنولوجيا المغنيسيوم ، التي تقام كل عام في الاجتماع والمعرض السنوي TMS ، واحدة من أكبر التجمعات السنوية لمتخصصي المغنيسيوم في العالم. يتم تقديم الأوراق في جميع جوانب المجال ، بدءًا من الإنتاج الأولي إلى التطبيقات إلى إعادة التدوير. علاوة على ذلك ، تستكشف الأوراق كل شيء من نتائج الأبحاث الأساسية إلى التصنيع. يغطي Magnesium Technology 2011 مجموعة واسعة من الموضوعات الحالية ، بما في ذلك السبائك وخصائصها ؛ منتجات الصب والمعالجة ؛ منتجات مشغولة ومعالجة؛ التشكيل والانضمام والتشغيل الآلي ؛ التآكل وتشطيب السطح ؛ علم البيئة. والتطبيقات الهيكلية. بالإضافة إلى ذلك ، ستجد تغطية للتطبيقات الجديدة والناشئة في مجالات مثل الطب الحيوي وتخزين الهيدروجين. 

Magnesium is a chemical element with the symbol Mg and atomic number 12. It is a shiny gray solid which bears a close physical resemblance to the other five elements in the second column (group 2, or alkaline earth metals) of the periodic table: all group 2 elements have the same electron configuration in the outer electron shell and a similar crystal structure.
المغنيسيوم هو عنصر كيميائي يحمل الرمز Mg والرقم الذري 12. وهو مادة صلبة رمادية لامعة تحمل تشابهًا ماديًا وثيقًا مع العناصر الخمسة الأخرى في العمود الثاني (المجموعة 2 ، أو معادن الأرض القلوية) من الجدول الدوري: الكل عناصر المجموعة 2 لها نفس التكوين الإلكتروني في غلاف الإلكترون الخارجي وبنية بلورية مماثلة.

Magnesium is the ninth most abundant element in the universe. It is produced in large, aging stars from the sequential addition of three helium nuclei to a carbon nucleus. When such stars explode as supernovas, much of the magnesium is expelled into the interstellar medium where it may recycle into new star systems. Magnesium is the eighth most abundant element in the Earth's crust and the fourth most common element in the Earth (after iron, oxygen and silicon), making up 13% of the planet's mass and a large fraction of the planet's mantle. It is the third most abundant element dissolved in seawater, after sodium and chlorine.
المغنيسيوم هو تاسع أكثر العناصر وفرة في الكون. يتم إنتاجه في النجوم الكبيرة والشيخوخة من الإضافة المتسلسلة لثلاث نوى هيليوم إلى نواة الكربون. عندما تنفجر مثل هذه النجوم على شكل مستعرات عظمى ، يتم طرد الكثير من المغنيسيوم إلى الوسط بين النجوم حيث يمكن إعادة تدويره إلى أنظمة نجمية جديدة. يعد المغنيسيوم ثامن أكثر العناصر وفرة في القشرة الأرضية  ورابع أكثر العناصر شيوعًا في الأرض (بعد الحديد والأكسجين والسيليكون) ، ويشكل 13٪ من كتلة الكوكب وجزءًا كبيرًا من غطاء الكوكب. وهو ثالث أكثر العناصر المذابة وفرة في مياه البحر ، بعد الصوديوم والكلور.

Experimental

Thixomolded 3mm thick plates of AXJ810, composition shown in
Table I, were warm rolled in one pass at an approximate
temperature of 250°C to a 50% reduction in thickness. The sheets
were then subjected a flattening treatment at 270°C for two
minutes. Additional heat treatments of varied duration below the
ß-solvus at 300°C and above the ß-solvus at 450°C. were then
conducted.

Abstract

Micro structure refinement via static and dynamic recrystallization
during thermomechanical processing is crucial to the development
of wrought magnesium product with desirable combinations of
strength and ductility. Micro structural evolution in thixomolded
AXJ810 is investigated during warm rolling and subsequent
annealing at 300°C and 450°C using scanning electron
microscopy and electron backscatter diffraction. The rolled sheets
exhibited a partially recrystallized micro structure with a strong
basal texture. Significant grain refinement was observed during
both static and dynamic recrystallization. Retarded grain growth
and strong texture randomization were observed only in regions
containing intermetallic particles.



سنة النشر : 2013م / 1434هـ .
حجم الكتاب عند التحميل : 0.7 ميجابايت .
نوع الكتاب : pdf.
عداد القراءة: عدد قراءة Magnesium Technology 2013: Recrystallization Behavior of a MgAlCa Alloy during Thermomechanical Processing and Subsequent Heat Treatment

اذا اعجبك الكتاب فضلاً اضغط على أعجبني
و يمكنك تحميله من هنا:

تحميل Magnesium Technology 2013: Recrystallization Behavior of a MgAlCa Alloy during Thermomechanical Processing and Subsequent Heat Treatment
شكرًا لمساهمتكم

شكراً لمساهمتكم معنا في الإرتقاء بمستوى المكتبة ، يمكنكم االتبليغ عن اخطاء او سوء اختيار للكتب وتصنيفها ومحتواها ، أو كتاب يُمنع نشره ، او محمي بحقوق طبع ونشر ، فضلاً قم بالتبليغ عن الكتاب المُخالف:

برنامج تشغيل ملفات pdfقبل تحميل الكتاب ..
يجب ان يتوفر لديكم برنامج تشغيل وقراءة ملفات pdf
يمكن تحميلة من هنا 'http://get.adobe.com/reader/'

المؤلف:
سوفين نايجل ماثودهو - Suveen N. Mathaudhu

كتب سوفين نايجل ماثودهو سوفين نايجل ماثودهو دكتور جامعى كرسي ، علوم وهندسة المواد مهندس ميكانيكى. المزيد..

كتب سوفين نايجل ماثودهو
الناشر:
The Minerals, Metals, & Materials Society
كتب The Minerals, Metals, & Materials Society.المزيد.. كتب The Minerals, Metals, & Materials Society
معنى اسمكتابة على تورتة الخطوبةزخرفة الأسماءالتنمية البشريةالكتابة عالصورالكتب العامة زخرفة أسامي و أسماء و حروف..كتب قصص و رواياتأسمك عالتورتهكورسات اونلاينحكم قصيرةشخصيات هامة مشهورةكتابة على تورتة مناسبات وأعيادكتب القانون والعلوم السياسيةOnline يوتيوبكتب الأدبFacebook Text Artمعاني الأسماءقراءة و تحميل الكتبكتابة على تورتة الزفافالمساعدة بالعربيكتب الطبخ و المطبخ و الديكوركتب التاريختورتة عيد ميلادخدماتكتب للأطفال مكتبة الطفلكتب تعلم اللغاتحكمةاقتباسات ملخصات كتبكتب اسلاميةزخرفة توبيكاتSwitzerland United Kingdom United States of Americaكورسات مجانيةكتب الروايات والقصصكتابة أسماء عالصوراصنع بنفسكبرمجة المواقعكتب السياسة والقانونمعاني الأسماءتورتة عيد الميلادحروف توبيكات مزخرفة بالعربيالقرآن الكريمالطب النبوي